KASTAR 116 Automotive PU Sealant – Durable & High-Performance
Kastar 115 Windshield/Auto Glass PU Sealant is chemically superior. It is perfect for commercial or industrial use as it is a one-part, non-sag polyurethane sealant. Curing occurs in contact with atmospheric moisture and it hardens to form an elastomer that is weather-stable. KASTAR 115 is produced in compliance with the ISO/TS 16949:2002, to maintain the quality standard and offer higher reliability in extreme operating conditions.
Appearance: Black homogeneous paste
Density (g/cm³): 1.50
Sagging properties (mm): 0
Shore A-hardness (A°): 45
Tack free time (min): 35
Tensile strength (Mpa): 2.8
Elongation at break (%): 420
1. Sealing & welding automobile glass and body.
2. Bonding of automobile fitting interior and exterior.
|
|
|
| Testing Items | Performance |
| Appearance | Black homogeneous paste |
| Density (g/cm³) | 1.50 |
| Sagging properties (mm) | 0 |
| Shore A-hardness (A°) | 45 |
| Tack free time (min) | 35 |
| Tensile strength (Mpa) | 2.8 |
| Elongation at break (%) | 420 |
| Tensile-share strength (Mpa) | ≥3.5 |
| Curing speed (mm/d) | 2.8 |
| Non-volatile contents (%) | 99 |
| Tear strength | 10 |
| Extrudability (ml/min) | 320 |
| Operating Temperature | -40 to 90 degrees C |
| Pollution | Non |
| Application temperature (ºC) | -5～+35 |
1. Sealing & welding automobile glass and body.
2. Bonding of automobile fitting interior and exterior.
|
|
|
| Testing Items | Performance |
| Appearance | Black homogeneous paste |
| Density (g/cm³) | 1.50 |
| Sagging properties (mm) | 0 |
| Shore A-hardness (A°) | 45 |
| Tack free time (min) | 35 |
| Tensile strength (Mpa) | 2.8 |
| Elongation at break (%) | 420 |
| Tensile-share strength (Mpa) | ≥3.5 |
| Curing speed (mm/d) | 2.8 |
| Non-volatile contents (%) | 99 |
| Tear strength | 10 |
| Extrudability (ml/min) | 320 |
| Operating Temperature | -40 to 90 degrees C |
| Pollution | Non |
| Application temperature (ºC) | -5～+35 |